Title: Preparation of High Photocatalyst Mesoporous TiO2 from Nanosheets Using Autoclave Unit (Thai Made)
Authors: A. Simpraditpan
T. Wirunmongkol
W. Boonwatcharapunsakun
S. Sakulkhaemaruethai
S. Pivsa-art
C. Duangduen
S. Pavasupree
Keywords: Hydrothermal
Photocatalytic Activity
Titanium Dioxide
Issue Date: 25-May-2011
Publisher: Rajamangala University of Technology Thanyaburi
Abstract: The aim of this study is to prepare mesoporous TiO2 from high specific surface area nanosheets by simple hydrothermal method at 120 ºC of 12 hrs using autoclave unit (Thai made). The shape, size (TEM), crystalline structure (XRD), BET-specific surface area and photocatalytic activity of the prepare samples were investigated. The XRD results revealed that the prepared nanosheets were amorphous phase. The specific surface area, average pore diameter and pore volume were 360.28 m2/g, 3-5 nm and 0.275 cm3/g, respectively. The crystalline structure of calcined nanosheets at 300-600 ºC was anatase TiO2 with decreasing in the specific surface area. The intensity of anatase TiO2 structure increased when the calcination temperature was increased. Moreover, the photocatalytic activity of the calcined nanosheets was higher than the as-synthesized nanosheets and commercial nano TiO2 (P-25, JRC-01, JRC-03). This preparation method provided a simple routh to fabricate nanosheets using autoclave unit (Thai made).
Appears in Collections:ประชุมวิชาการ (Proceedings)

Files in This Item:
File Description SizeFormat 
NM08r.pdfPreparation of High Photocatalyst Mesoporous TiO2 from Nanosheets Using Autoclave Unit (Thai Made)642.35 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.