Title: Preparation of Knitting Socks from Poly)lactic acid ( and )Poly[)R(-3-hydroxybutyrate-co-)R(-3-hydroxyvalerate]) PHBV( blends for Textile Industrials
Authors: S. Pivsa-Art
N. Srisawat
N. O-Charoen
S. Pavasupree
W. Pivsa-Art
Keywords: Biodegradable plastics
Melt spinning
Issue Date: 25-May-2011
Publisher: Rajamangala University of Technology Thanyaburi
Abstract: The PLA/PHBV blends were prepared using dry blend in the melt spinning method. The ratios of PLA:PHBV were varied with 100:0, 95:5, 90:10, 85:15 and 80:20 wt%. The temperature of single screw extruder was set at 210 to 235°C with screw speed 9 rpm and free fall at draw speed 450, 500 and 550 m /min. The textile fibers were subjected to thermal, morphology and mechanical property evaluation. The results show that the addition of PHBV was compatible with PLA in the textile fibers and increased the flexibility of the blends. The ratios of PLA/PHBV at 95/5 and 90/10 was used for the preparation of knitting socks. The Sonic velocity and Tenacity of the fiber was found to be 2.37% and 0.93 CN /den, respectively.
URI: http://www.repository.rmutt.ac.th/dspace/handle/123456789/477
Appears in Collections:ประชุมวิชาการ (Proceedings)

Files in This Item:
File Description SizeFormat 
NM50r.pdfPreparation of Knitting Socks from Poly)lactic acid ( and )Poly[)R(-3- hydroxybutyrate-co-)R(-3-hydroxyvalerate]) PHBV( blends for Textile Industrials226.65 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.